聚对苯二甲酸乙二酯

Kuraray America, Inc.

Technical Data

 

产品说明

 

KURARISTER™ N, OPA-Based high barrier film for retorted packaging.

 

Building on the concept of creating an excellent barrier film with high transparency, easy processing and easy printing, Kuraray Co., Ltd. has created a superb OPA oriented gas barrier film for retort applications with KURARISTER™ N.

 

KURARISTER™ N is a 15 µm oriented polyamide (OPA) film, coated on both sides with special barrier layers (1 µm each) developed by Kuraray. These thin but extremely durable coating layers display gas barrier properties that are signifi cantly better than standard OPA film before and after retort.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet (English)

搜索 UL 黄卡 • Kuraray America, Inc.

供货地区 • 北美洲 • 欧洲

• 南美洲 • 亚太地区

性能特点 • 极佳的可印刷性 • 可加工性，良好 • 食品接触的合规性

• 抗穿孔性 • 耐用性 • 阻隔树脂

用途 • 薄膜 • 层压板 • 非特定食品应用

外观 • 清晰/透明

形式 • 颗粒料

薄膜 额定值 单位制 测试方法

膜刺穿强度 (1.0 µm) 0.686J

膜刺穿力 (1.0 µm) 7.20N

割线模量 ASTM D882

MD: 1.0 µm 3700MPa

TD: 1.0 µm 3600MPa

抗张强度 ASTM D882

MD: 断裂, 1.0 µm 190MPa

TD: 断裂, 1.0 µm 190MPa

伸长率 ASTM D882

MD: 断裂, 1.0 µm 80%

TD: 断裂, 1.0 µm 87%

透氧率 (20°C, 1.0 µm, 85% RH) cm³•mm/m²/atm/24 ASTM D3985

0.50 hr

补充信息

Tensile Modulus,after retort, MD: 2600 MPa

Tensile Modulus, after retort, TD: 2400 MPa

Elongation @ Break, ASTM D882, 1µ, after retort, MD: 89%

Elongation @ Break, ASTM D882, 1µ, after retort, TD: 81%

Tensile Strength @ Brk, ASTM D882, 1 µ, after retort, MD: 190 MPa

Tensile Strength @ Brk, ASTM D882, 1 µ, after retort, TD: 180 MPa

Wetting Idex, 23°C, 50% RH: >54 dyne/g

Film Puncture Energy, 1 µ, after retort, 120°C, 30 min, N side: 10.8 kg cm

Film Puncture Energy, 1 µ, after retort, 135°C, 60 min, N side: 8 kg cm

Film Puncture Energy, 1 µ, after retort, 120°C, 30 min, CPP side: 8.8 kg cm

Film Puncture Energy, 1 µ, after retort, 120°C, 30 min, CPP side: 6.5 kg cm

Film Puncture Energy, 1 µ, laminate before retort, N side: 10.0 kg cm

Film Puncture Energy, 1 µ, laminate before retort, CPP side: 8.2 kg cm

Film Puncture Force, 1 µ, laminate before retort: 8.5 N

Film Puncture Force, 1 µ, after retort, 120°C, 30 min: 8.6 N

Film Puncture Force, 1 µ, after retort, 135°C, 60 min: 8.3 N

Oxygen Permeability, 1 µ, laminate before retort, 20°C, 85% RH: 0.6 cc/m².day.atm

Oxygen Permeability, 1 µ, after retort, 20°C, 85% RH: 0.7 cc/m².day.atm

 

 

 

 

 

 

 