13549213581 肖生

 

高光, 高强度, 包装, 薄膜, 清晰度高

 

OxyShield® 1545

聚酰胺6

Honeywell

 

Technical Data

 

产品说明

 

Oxyshield®1545 is a 0.59 mil (15 micron) biaxially oriented nylon 6 film coated on one side with PVdC. The coating is applied without the need for a primer layer and so presents superior coating adhesion and laminating adhesion to other films. Medium oxygen and moisture vapor barrier and superior clarity are properties well suited for packaging applications requiring excellent mechanical strength and long shelf life.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet (English)

搜索 UL 黄卡 •  Honeywell

供货地区 • 北美洲

特性 • 高光 • 高强度 • 清晰度，高

用途 • Bi-axially Oriented Film • 包装

形式 • 薄膜

 

机械性能 额定值单位制 测试方法

摩擦系数 ASTM D1894

与金属 - 动态, 挤出涂覆 0.55

与金属 - 动态 0.30

与金属 - 静态 0.40

与金属 - 静态, 挤出涂覆 1.3

与自身 - 动态 0.65

与自身 - 静态 1.1

薄膜 额定值单位制 测试方法

薄膜厚度 - 经测试 15µm

割线模量 ASTM D882

MD : 15 µm 2320MPa

TD : 15 µm 2150MPa

抗张强度 ASTM D882

MD : 断裂, 15 µm 248MPa

TD : 断裂, 15 µm 248MPa

伸长率 ASTM D882

MD : 断裂, 15 µm 87%

TD : 断裂, 15 µm 87%

透氧率 (23°C, 15 µm, 65% RH) cm³•mm/m²/atm/24 ASTM D3985

0.35 hr

水气透过率 (15 µm, 38°C, 100% RH) 12g•mm/m²/atm/24 hr ASTM F1249

光学性能 额定值单位制 测试方法

雾度 (15.0 µm) < 5.0% ASTM D1003

补充信息

Yield: 40800 in²/lb

Tensile Strength @ Break, ASTM D 882, MD: 34000 to 38000 psi

Tensile Strength @ Break, ASTM D 882, TD: 34000 to 38000 psi

Elongation @ Break, ASTM 882, MD: 75 to 100%

Elongation @ Break, ASTM 882, TD: 75 to 100%

Secant Modulus, ASTM D 882, MD: 300000 to 375000 psi

Secant Modulus, ASTM D 882, TD: 275000 to 350000 psi

Graves Tear (initial), ASTM D 1004, MD: 1100 to1400 g/mil

Graves Tear (initial), ASTM D 1004, TD: 1100 to1400 g/mil

Coefficient of Friction, ASTM D 1894: 0.6 to 0.7 vs Itself-Dynamic

Coefficient of Friction, ASTM D 1894: 0.9 to 1.3 vs Itself-Static

Coefficient of Friction, ASTM D 1894: 0.2 to 0.4 vs Metal-Dynamic

Coefficient of Friction, ASTM D 1894: 0.3 to 0.5 vs Metal-Static

Coefficient of Friction, ASTM D 1894, Extrusion Coated: 0.4 to 0.7 vs Metal-Dynamic

Coefficient of Friction, ASTM D 1894, Extrusion Coated: 0.8 to 1.8 vs Metal-Static

Dimensional Stability, ASTM D1204, MD, 320°F, 5min: < 2.5% shrinkage

Dimensional Stability, ASTM D1204, TD, 320°F, 5min: <1.5% shrinkage

 

 

 

 

 